Tig Filler Rod For Welding Sheet Metal Pans

Stainless steel mild steel copper alloys aluminum alloys nickel alloys titanium alloys.

Tig filler rod for welding sheet metal pans.

The thin filler rod allows you to make a very small puddle and takes very little heat to flow melt the filler rod into the weld puddle. Works like a champ. Don t overheat the puddle just make it sweat. For sheet metal up to 1 8 inch thick do not use a welding rod bigger than the thickness of the metal you re welding.

I use a 1 16 red electrode and either 030 or 035 tig filler rod. 4047 contains 12 silicon. 4043 aluminum tig rod the most versatile for 3003 6061 a355 aluminum castings etc. The only other thing that would work is ss filler.

The thickness of the material you will be welding also determines the required diameter of the filler rod. Filler rod in tig welding you feed the filler rod into the molten puddle by hand. Choose the right size tig welding rod. Use 5356 on 6061 when the weld will be anodized after welding.

Cut lengths are 36 long. Er308l stainless steel tig filler rods 10 lb. So say you are welding 18 gauge sheet metal that would be 0 0478 in decimal so i would set my machine at 48 amps. You don t want the bronze to mix with the base metal.

Lets say i m welding 1 8 thick metal that would be 0 1250 in decimal so i would. On the above panel i used a 3 32 2 ceriated tungsten and 1 16 filler rod but i prefer a 1 16 2 ceriated tungsten and a 1 16 filler on sheetmetal. Less heat input means less anealing of the part. The amperage is low and the weld puddle needs to be small to prevent blowing a hole.

Tig welding filler rod high performance tig welding filler metal for every application the most complete line of high quality washington alloy brand 36 cut length filler metal for virtually every tig welding brazing application. This is an application for silicon bronze tig rod. Eureka 27 is a premium quality ac dc low hydrogen iron powder electrode. It is used in the general fabrication or joining of structural steels pipes plates and pressure vessels.

When you dip the rod into the puddle the rod sucks the heat from the puddle making it hard to. I tig braze hss to stress proof shanks all the time. This is nice for thin gauge butt welds like we re showing here. And do yourself a favor and get some 4047 rod for castings where porosity rares its ugly head.

Er308l stainless steel filler rod is suitable for general stainless steel welding applications of all type 304 304l 308 308l 312 and 347 materials.